Effect of the capping on the local Mn oxidation state in buried (001) and (110) SrTiO3/La2/3Ca1/3MnO3 interfaces

The electronic stability of (001) and (110) surfaces of La2/3Ca1/3MnO3 (LCMO) capped with nanometric SrTiO3 (STO) layers in epitaxial heterostructures is addressed by (S)TEM electron energy loss spectroscopy. It is found that growth of STO on (001)LCMO promotes a significant electron doping of LCMO that extends a few nanometers deep into the film. In contrast, (110)LCMO appears to be electronically more robust and no electronic reordering has been observed. These results are in clear correlation with the distinct magnetic properties observed in those interfaces and illustrate that complex chemical phenomena take place at interfaces among multivalent oxides. VC 2011 American Institute of Physics.

Tipus de document

Article

Versió publicada

Llengua

Anglès

Matèries i paraules clau

Espectroscòpia de pèrdua d'energia d'electrons; Propietats magnètiques; Nanociència; Compostos inorgànics; Electron energy loss spectroscopy; Magnetic properties; Nanoscience; Inorganic compounds

Publicat per

American Institute of Physics

Documents relacionats

Reproducció del document publicat a: http://dx.doi.org/10.1063/1.3660786

Journal of Applied Physics, 2011, num. 110, p. 103903-1-103903-5

http://dx.doi.org/10.1063/1.3660786

Citació recomanada

Aquesta citació s'ha generat automàticament.

Exportar

DIDL MARC MARC_CCUC METS OAI_DC ORE QDC RDF

Drets

Aquest element apareix en la col·lecció o col·leccions següent(s)

Enginyeria Electrònica i Biomèdica [781]

ISGlobal - Institut de Salut Global de Barcelona [60793]