We report on the structural, mechanical, and thermal analysis of 40 nm thick polystyrene-block-poly(ethylene oxide) (PS-b-PEO) block copolymer (BCP) films coated with evaporated chromium layers of different thicknesses (1, 2, and 5 nm). Solvent annealing processes allow the structural control of the BCP films morphology by rearranging the position of the PEO cylinders parallel to the substrate plane. High-vacuum scanning thermal microscopy and ultrasonic force microscopy measurements performed in ambient pressure revealed that coated ultrathin metal layers strongly influence the heat dissipation in the BCP films and the local surface stiffness of the individual BCP domains, respectively. The measured tip-sample effective thermal resistance decreases from 6.1 × 107 to 2.5 × 107 K W-1 with increasing Cr film thickness. In addition, scanning probe microscopy measurements allow the thermal and mechanical mapping of the two segregated polymer domains (PEO-PS) of sub-50 nm characteristic sizes, with sub-10 nm thermal spatial resolution. The results revealed the effect of the surface morphology of the BCP and the incorporation of the metal film on the nanoscale thermal properties and volume self-assembly on the mechanical properties. The findings from this study provide insight into the formation of high aspect ratio BCP-metal structures with the more established applications in lithography. In addition, knowledge of the thermal and mechanical properties at the nanoscale is required in emergent applications, where BCPs, or polymers in general, are part of the structure or device. The performance of such devices is commonly related to the requirement of increased heat dissipation while maintaining mechanical flexibility.