Títol:
|
Magnetic properties of Fe-Cu-Nb-Si-B nanocrystaliine magnetic alloys
|
Autor/a:
|
García del Muro y Solans, Montserrat; Batlle Gelabert, Xavier; Zquiak, R.; Tejada Palacios, Javier; Polak, C.; Grössinger, R.
|
Altres autors:
|
Universitat de Barcelona |
Abstract:
|
Several ribbons of composition Fe73.5Cu1Nb 3Si16.5B6 and Fe73.5Cu1 Nb3Si13.5B9 were prepared by annealing the as-quenched samples between 525°C and 700°C; which induced nucleation of nanocrystallites of Fe bcc-type composition. Mean grain sizes were obtained from X-ray diffraction. Static magnetic properties were measured with both a Magnet Physik Hysteresis-Graph (up to 200 Oe) and a SHE SQUID magnetometer (up to 50 kOe). Soft magnetic parameters (coercive field and initial permeability) were very sensitive to grain size. The ZFC magnetization at low field showed a broad peak at a temperature TM, thus signalling a certain distribution of nanocrystalline sizes, and TM strongly decreased when the mean grain size decreased. Isothermal magnetization curves at low temperature showed the expected asymptotic behavior of a random magnet material at low and high fields. |
Matèries:
|
-Difracció de raigs X -Materials magnètics -Aliatges -Magnetisme -Materials nanoestructurats -X-ray diffraction -Magnetic materials -Alloys -Magnetism -Nanostructured materials |
Drets:
|
(c) IEEE, 1994
|
Tipus de document:
|
Article Article - Versió publicada |
Publicat per:
|
IEEE
|
Compartir:
|
|