CoFe2O4 nanoparticles are added to magnesium hydride (MgH2) by high-energy ball milling in order to improve its hydriding properties. The hydrogen storage properties and catalytic mechanism are investigated by pressure-composition-temperature (PCT), differential thermal analysis (DTA), X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). The nonisothermal desorption results show that the onset desorption temperature of the MgH2 + 7 mol% CoFe2O4 is 160 degrees C, which is 200 degrees C lower than of the as-received MgH2. The dehydrogenation process of the MgH2 doped with the CoFe2O4 nanoparticles includes two steps. DTA curves and XRD patterns reveal that a chemical reaction happens between MgH2 and CoFe2O4, forming the final products of the ternary combination, corresponding to Co3Fe7, MgO and Co. The onset desorption temperature of the ball-milled MgH2 doped with Co3Fe7, MgO and Co is about 260 degrees C, approximately 100 degrees C lower than the un-doped MgH2, demonstrating that the ternary combination (Co3Fe7, MgO, and Co) also has a great catalytic effect on the MgH2 hydrogen storage properties. It is also confirmed that the various methods of adding the ternary combination have different effects on the MgH2 hydriding-dehydriding process. (C) 2014 Elsevier B.V. All rights reserved.

Peer Reviewed