Enhanced reliability of yttria-stabilized zirconia for dental applications
Camposilvan, Erik; García Marro, Fernando; Mestra Rodriguez, Alvaro; Anglada Gomila, Marc
Universitat Politècnica de Catalunya. Departament de Ciència dels Materials i Enginyeria Metal·lúrgica; Universitat Politècnica de Catalunya. CIEFMA - Centre d'Integritat Estructural i Fiabilitat dels Materials
An increasing number of dental applications based on yttria-stabilized zirconia (3Y-TZP) have been developed in recent years as a result of the advances and versatility of dry-processing and soft machining at the pre-sintered state. Nonetheless, the long-term surface stability of these materials in humid environment is still a matter of concern and may limit its application. In this work, a simple method to prevent hydrothermal degradation on zirconia surface is studied in detail. This method involves the infiltration of pre-sintered parts with optimized solutions containing Ce salts, leaving unchanged the other processing steps, allowing the diffusion of Ce during conventional sintering. Several pre-sintering conditions, solution concentrations and sintering temperatures were studied and characterized, obtaining working parameters for the production of zirconia parts with mechanical properties similar to standard 3Y-TZP and high resistance to hydrothermal aging. This optimal combination was obtained with the 1150 ºC pre-sintering temperature, 50 wt% solution and sintering at 1450 ºC, leading to a superficial CeO2 content of about 3 mol%.
Àrees temàtiques de la UPC::Enginyeria dels materials
Àrees temàtiques de la UPC::Enginyeria dels materials
Dental Implants
Infiltration
Zirconia
Low Temperature Degradation
Dental implant
Ceria
3Y-TZP.
Implants artificials
Zirconi
http://creativecommons.org/licenses/by-nc-nd/3.0/es/
info:eu-repo/semantics/submittedVersion
Artículo
         

Mostrar el registro completo del ítem

Documentos relacionados

Otros documentos del mismo autor/a

Camposilvan, Erik; Flamant, Quentin Jean Alain; Anglada Gomila, Marc
Camposilvan, Erik; Torrents Abad, Oscar; Anglada Gomila, Marc
García Marro, Fernando; Camposilvan, Erik; Mestra Rodríguez, Álvaro Miguel; Anglada Gomila, Marcos Juan
García Marro, Fernando; Camposilvan, Erik; Anglada Gomila, Marcos Juan
Camposilvan, Erik; García Marro, Fernando; Maspero, F.; Cuspidi, G.; Anglada Gomila, Marcos Juan