Scaffolds constituted by mixed polylactide and poly(ethylene glycol) electrospun microfibers
Llorens Domenjó, Elena; Bellmunt Montoya, Sergi; Valle Mendoza, Luis Javier del; Puiggalí Bellalta, Jordi
Universitat Politècnica de Catalunya. Departament d'Enginyeria Química; Universitat Politècnica de Catalunya. PSEP - Polimers Sintètics: Estructura i Propietats. Polimers Biodegradables.
Scaffolds comprising different ratios of poly(ethylene glycol) (PEG) and polylactide (PLA) electrospun fibers were prepared by using a single rotary collector. Electrospinning parameters and solution conditions were optimized to obtain continuous fibers and a homogeneous distribution of both polymers in the final scaffold. Short needle-collector distances allowed good overlapping of the two incident and independent jets. The composition of the scaffold was effectively tuned by varying the flow rate of the PLA solution. PEG and PLA fibers could be well distinguished in the scaffold because of their smooth and rough texture, respectively, and diameters in the nanometer and micrometer range. Greater sizes corresponded to polylactide and clearly depended on the flow rate. Drugs such as triclosan and polyhexamethylene biguanide hydrochloride, which have different hydrophilic/hydrophobic character and molecular size, were loaded into PLA microfibers by electrospinning. The high water solubility of PEG justified its use as a sacrificial polymer. Thus, it was possible to prepare scaffolds with tuned porosity (from 40 to 80 %) by water immersion of dual samples having different PEG content. Porosity greatly affected the release rate; specifically, a practically instantaneous or a sustained release was determined for triclosan in an appropriate medium. Drug loaded scaffolds had a clear bactericidal effect that was more effective for Gram-positive bacteria. Cell proliferation studies indicate that fibroblast colonization increased by 20-25 % in PLA/PEG scaffolds with high PEG contents compared to the control, whereas this effect was not observed for epithelial cells.
Peer Reviewed
Àrees temàtiques de la UPC::Enginyeria química
Polymers
Electrospinning
Electrospinning
Polylactide
Poly(ethylene glycol)
Sacrificial polymer
Triclosan
Biguanide
Drug release
Biocompatibility
HYBRID FIBROUS SCAFFOLDS
POLYMER NANOFIBERS
FIBERS
ACID)
MIXTURES
EMULSION
Polímers
Fibres tèxtils sintètiques
Attribution-NonCommercial-NoDerivs 3.0 Spain
http://creativecommons.org/licenses/by-nc-nd/3.0/es/
info:eu-repo/semantics/publishedVersion
Artículo
         

Mostrar el registro completo del ítem

Documentos relacionados

Otros documentos del mismo autor/a

Llorens Domenjó, Elena; Armelín Diggroc, Elaine Aparecida; Pérez Madrigal, Maria del Mar; Valle Mendoza, Luis Javier del; Alemán Llansó, Carlos; Puiggalí Bellalta, Jordi
Llorens Domenjó, Elena; Valle Mendoza, Luis Javier del; Puiggalí Bellalta, Jordi
Díaz Andrade, Angélica María; Franco García, María Lourdes; Casas Becerra, María Teresa; Valle Mendoza, Luis Javier del; Aymami Bofarull, Juan; Olmo Osuna, Cristian; Puiggalí Bellalta, Jordi
Bertran Cànovas, Òscar; Valle Mendoza, Luis Javier del; Revilla López, Guillermo; Rivas Cañas, Manuel; Chaves Barboza, Gustavo Adolfo; Casas Becerra, María Teresa; Casanovas Salas, Jordi; Turon Dols, Pau; Puiggalí Bellalta, Jordi; Alemán Llansó, Carlos
Planellas Oates, Marc; Pérez Madrigal, Maria del Mar; Valle Mendoza, Luis Javier del; Kobauri, Sophio; Katsarava, Ramaz; Alemán Llansó, Carlos; Puiggalí Bellalta, Jordi